Essays about: "Hydrogen embrittlement"

Showing result 1 - 5 of 13 essays containing the words Hydrogen embrittlement.

1. 1. Evaluation of Crack Depth Meter - An investigation of the crack depth meters possibilities and limitations for commonly occurring damage mechanisms

   University essay from KTH/Hållfasthetslära

   Author : Alfred Norberg; [2023]
   Keywords : Crack depth measurement; RMG 4015; ACPD; Damage Mechanism; Evaluation; FEM Simulation; Sprickdjupsmätning; RMG 4015; ACPD; Skademekanism; Utvärdering; FEM-simulering;

   Abstract : In this master thesis, the accuracy of the crack depth meter RMG 4015 was evaluated for different types of cracks with various damage mechanisms. In total, 61 crack depth measurements were conducted with the crack depth meter on 56 cracks which were located in the 23 different test pieces supplied by Kiwa. READ MORE

3. 2. SFEER Hydrogen Permeation : Finding a suitable coating for the PA6 liner

   University essay from Uppsala universitet/Institutionen för materialvetenskap

   Author : Elsa Friis; Klara Karlsson; Rebecka Damgren; Emma Åkesson; Malin Johansson; [2023]
   Keywords : Hydrogen permeation; PA6; coating; hydrogen permeation barrier; polymer hydrogen permeation; permeation; protective coating; hydrogen embrittlement;

   Abstract : Water Stuff & Sun are developing a hydrogen battery based on a technology called SFEER’s. The SFEER’s are spherical high-pressure gas storage containers that are the size of a tennis ball. They consist of a carbon fiber-shell that is lined on the inside with a polymer called PA6. READ MORE

4. 3. Design of a test rig for in situ hydrogen charging of rolling element bearings under load

   University essay from Luleå tekniska universitet/Maskinelement

   Author : Oskar Moström; [2023]
   Keywords : tribology; hydrogen embrittlement; mechanical engineering; rolling element bearing; machine elements; design; mechanical design; CAD; mechanical construction; construction; material science; Tribologie; Wasserstoffversprödung; Maschinenbau; Wälzlager; Maschinenelemente; Design; Maschinenkonstruktion; CAD; mechanischer Bau; Konstruktion; Materialwissenschaft; tribologi; väteförsprödning; maskinteknik; rullningselementlager; maskinelement; design; mekanisk design; CAD; mekanisk konstruktion; konstruktion; materialvetenskap; lager;

   Abstract : This Master's thesis is part of the Hydrogen Embrittlement in Rolling element bearings project (HERo) initiated at Luleå University of Technology (LTU), with the primary objective of determining critical hydrogen concentrations in bearing steel for rolling element bearings. The specific aim of this Master's thesis is to design a test rig that enables the investigation of the effects of hydrogen embrittlement on rolling element bearings under load. READ MORE

5. 4. Effect of Proton Irradiation on the Mechanical Properties of Fe-10Cr-4Al in Liquid Lead

   University essay from KTH/Fysik

   Author : Gabriela Lapinska; [2023]
   Keywords : Fe-10Cr-4Al; Lead; Radiation Damage; Slow Strain Rate Testing; Fe-10Cr-4Al; bly; strålskador; Slow Strain Rate Testing;

   Abstract : Among the structural materials under consideration for future lead-cooled fastreactors, special attention is paid to ferritic Fe-10Cr-4Al due to its superior corrosionand erosion protective properties, as well as its insensitivity to liquid metalembrittlement in liquid lead. This thesis gives an inside look into the radiation damageproperties of the alloy and the possible embrittlement scenarios. READ MORE

6. 5. Influence of hydrogen and carbides on high temperature cracking in cast Inconel

   University essay from Uppsala universitet/Tillämpad mekanik

   Author : Gunnar Dufwa; [2022]
   Keywords : Hydrogen embrittlement; carbide; finite element method; dislocation dynamics;

   Abstract : Hydrogen embrittlement is a well-known source of cracking in metallic mechanical elements. This work studies the influence of hydrogen and carbides on the crack formation in a castnickel-alloy-component in a selective catalytic reduction system. READ MORE