Surface Analysis of Aluminium Alloy AA3003 Exposed to Immersion Corrosion Test : An X-Ray Photoelectron Spectroscopy Study

Abstract: Corrosion is a common issue which must be accounted for when designing all metal products in our society. Many factors need to be considered when new alloys are created, and further knowledge of the corrosion process would be of great use for companies worldwide. The purpose of this thesis was to investigate if X-ray Photoelectron Spectroscopy, XPS, can be used to characterise and quantify corrosion products. With the goal to develop a method that can be used for further studies to increase our understanding of the corrosion process. Aluminium alloy AA3003 was subjected to an immersion corrosion test in an acidified salt solution for different periods of time and the produced chemical compounds were characterised using XPS. The results revealed a direct connection between corrosion time and formed product, which after characterisation proved to be aluminium hydroxide, Al(OH)3. It was concluded that XPS can be used for corrosion studies and is a method that shows great potential and should be further developed.