High temperature tribological evaluation of a self-lubricating laser cladding with and without external solid lubricant

Abstract: The purpose of the project work was to build knowledge of the tribological behaviour of self-lubricating laser cladding, with and without external solid lubricant during conditions relevant for hot metal forming of aluminium. The materials used during the project were plates coated with a Ni-based self-lubricating clad and a reference sample of work tool steel. The self-lubricating laser clad was applied using a high power direct diode laser. The external solid lubricant used was a graphite dispersion. The external solid lubricant was applied on the samples using a spraying technique, leaving a dry layer of solid graphite on the plates. To test the tribological behaviour of the plates, linear reciprocating friction and wear tests were performed both under lubricated and dry conditions. During the dry tests, different surface roughness of the plates where investigated. The pins for the tribological test were made of AA7075. Parameters chosen for the tribological tests were based on conditions during hot forming of aluminium. After having taken images of the plates using scanning electron microscopy, and using a 3D optical profiler, the wear volume and material transfer was evaluated, and wear mechanism analysis was performed.   The tribological behaviour of polished Ni-based laser clad under dry conditions is comparable to that of the reference sample at its best performance. Using a mirror polished Ni-based laser clad under dry condition can be an option to not using external solid lubricant during hot forming of aluminium. Also, the surface roughness of the self-lubricating clad under dry conditions does not affect the coefficient of friction.