The Effect of Temperature Gradients During Intercritical Annealing of Advanced High Strength Steels : Method Development for Experimental Streamlining

Abstract: The third-generation advanced high strength steels, AHSS, represent an opportunity for today’s steel development, where lighter materials with maintained strength and toughness are in demand. The unique properties of these materials often stem from a tailored microstructure. In the continued development of these steels, without relying on expensive alloying methods, process design in the form of precise heat treatments plays an increasingly important role. This work focuses on Medium Mn AHSS with the aim of investigating one of these heat treatments, intercritical annealing, which is essential for achieving the desired material properties. Experimental testing of annealing effects is acknowledged to be a challenging process, and this study aims to present a novel approach for these types of tests. During experimental testing of intercritical annealing, the thermomechanical testing system Gleeble 3800 is a recognized tool. The mounting technique employed in the Gleeble results in an inhomogeneous heat distribution in the samples, generating a thermal gradient. This report aims to utilize this gradient as an opportunity to test the effect of several intercritical annealing temperatures on one sample, thereby increasing the efficiency of experimental work. The method is based on data retrieved from thermocouples attached to the specimen during Gleeble trials with the intent to identify the thermal gradient. This data is combined with x-ray diffraction measurements where the retained austenite fraction is measured. Thermodynamic calculations of expected retained austenite fraction following intercritical annealing are performed parallel to experimental work. The results of this work show that it is possible to utilize the thermal gradient to retrieve extensive data regarding the effect of intercritical annealing using only one sample. The results show a distinct thermal gradient and a corresponding gradient of retained austenite fraction along the specimen. The results for retained austenite fraction at room temperature can be rationalized on the basis of computational predictions. These variations potentially arise due to the material not reaching equilibrium within the annealing timeframe. This conclusion is supported by other computational results concerning austenite composition. In summary, the present work illustrates a new approach streamlining experimental work that, with some refinements, has the potential to benefit the broader scienitific community, in addition to providing a powerful new tool for rapid technological advancement in the steel industry