16. Managing distortion in welded structures using FEM
University essay from KTH/LättkonstruktionerAbstract : Welding as high productive joining method is widely employed in automotive, aerospace and shipbuilding industries. In practice, welding distortion brings about undesirable effects on production accuracy, appearance and strength of welded components. READ MORE
-
17. Design and development of a testing device for a new invented Doctor Blade
University essay from Avdelningen för maskin- och materialteknikAbstract : This thesis project is about designing and developing an already existing testing device for a new invented Doctor Blade. A doctor blade is a blade used for creping tissue paper of a rotating cylinder, Yankee Cylinder. The old testing device was incomplete in a way that a rotating cylinder was missing, hence the tested blade is not loaded properly. READ MORE
-
18. Development of a Folding Boat Anchor
University essay from KTH/Maskinkonstruktion (Inst.)Abstract : This report is the result from a Master of Science Thesis work at the Royal Institute of Technology, and is executed by technology student Kristina Ahlinder for the behalf of Design Company Top Notch Design AB. Top Notch Design wants to expand their range of marine products and look in to the market of boat anchors. READ MORE
-
19. Effect of material grade on fatigue strength and residual stresses in high strength steel welds
University essay from KTH/LättkonstruktionerAbstract : This thesis work is concerned with effect of material grade on fatigue strength of welded joints. Fatigue strength evaluation of welded joints in as welded and post weld treated condition was carried out with effective notch method. Results of peak stress method have also been compared with those of effective notch method for as welded joints. READ MORE
-
20. Investigation on static strength of welded joints
University essay from KTH/MaterialvetenskapAbstract : Although high strength steels represent yield strength up to 1300 MPa, welded structures reveal lowerstrength values. The strongest commercially available electrode provides the yield strength of about900 MPa. Therefore, in welded steels with strength above this type of filler metal, achieving anacceptable global strength is a crucial issue. READ MORE