6. Heat Treatment and Secondary Phase Formation in FeCrNi Medium Entropy Alloys
University essay from KTH/MaterialvetenskapAbstract : The topics of high entropy alloys (HEA) and medium entropy alloys (MEA) have been heavily researched in recent years. A HEA usually consists of five or more base elements, and a MEA would have three or four base elements. READ MORE
-
7. Built-up edge formation in stainless steel milling
University essay from KTH/MaterialvetenskapAbstract : Milling tests were performed in stainless steel to investigate the formation of built-up edge (BUE). Three variants of tests were conducted which were divided as high-, medium, and low temperature milling tests. These tests were run in the austenitic stainless steel SS2343. READ MORE
-
8. Investigation of Microstructure and Mechanical Properties in Hot-work Tool Steels
University essay from KTH/MaterialvetenskapAbstract : Hot-work tool steels make up an important group of steels that are able to perform with good strength and toughness properties at elevated temperatures and stresses. They are able to gain this behavior through their alloy composition and heat treatment, which relies on the precipitation of alloy carbides to counter the loss in strength as the tempered material becomes more ductile. READ MORE
-
9. Characterization of Laser Deposited Alloy 718
University essay from KTH/MaterialvetenskapAbstract : Additive Manufacturing (AM) is a method of producing three-dimensional objects using additive processes. It allows great flexibility in the processes and reduces the design-to-production time. Laser Metal Deposition (LMD) is one of AM methods under development and is based on the deposition technology. READ MORE
-
10. Shear spinning of nickelbased super alloys and stainless steel
University essay from Högskolan Väst/Avdelningen för maskinteknik och naturvetenskapAbstract : Shear spinning of Haynes 282, Alloy 718, Alloy 600 and AISI 316L was done using several tool feeds and mandrel clearances. Multi passing of the materials was limited due to strain hardening and circumferential cracking except for AISI 316L. READ MORE